[1]操光辉,李军,沈光骏,等.硅酸铝短纤维增强铝硅合金复合材料的强度特性与界面结构[J].东南大学学报(自然科学版),1998,28(2):105-108.[doi:10.3969/j.issn.1001-0505.1998.02.020]
　Cao Guanghui Li Jun Shen Guangjun Wu Shenqing Shu Guangji,Mechanical Strength Characters and Interface Structure of Aluminosilicate Short Fibre Reinforced Al Si Alloy Composite[J].Journal of Southeast University (Natural Science Edition),1998,28(2):105-108.[doi:10.3969/j.issn.1001-0505.1998.02.020]
点击复制

硅酸铝短纤维增强铝硅合金复合材料的强度特性与界面结构()
分享到：

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
28
期数:
1998年第2期
页码:
105-108
栏目:
出版日期:
1998-03-20

文章信息/Info

Title:
Mechanical Strength Characters and Interface Structure of Aluminosilicate Short Fibre Reinforced Al Si Alloy Composite
作者:
操光辉;  李军;  沈光骏;  吴申庆;  舒光冀
东南大学材料科学与工程系； 东南大学分析测试中心
Author(s):
Cao Guanghui 1 Li Jun 1 Shen Guangjun 2 Wu Shenqing 1 Shu Guangji 1
1 Department of Materials Science and Engineering,Southeast University, Nanjing 210096
2 Analysis and Test Center, Southeast University, Na
关键词:
Al2O3·SiO2短纤维;  Al基复合材料;  强度;  界面结构
分类号:
材料科学与工程
DOI:
10.3969/j.issn.1001-0505.1998.02.020
摘要:
用挤压铸造法制备硅酸铝短纤维(Al2O3·SiO2)增强铝硅(Al Si)合金复合材料，测试了复合材料的室温及高温强度，并利用透射电镜观察了Al2O3·SiO2纤维与Al Si合金基体界面．结果表明：3％～10％的硅酸铝短纤维的加入使复合材料的室温及高温强度大大提高，在硅酸铝纤维与基体界面上存在两种反应物：一种物质是MgAl2O4，另一种物质含有Si和P，且二者原子之比为3∶4，呈正交结构，点阵常数为a＝0．714nm，b＝1．428nm，c＝2．409nm．