[1]孙瑜,廖恒成,孙国雄.Zr对Sr变质近共晶Al-Si铸造合金组织的影响[J].东南大学学报(自然科学版),2000,30(6):47-51.[doi:10.3969/j.issn.1001-0505.2000.06.011]
 Sun Yu,Liao Hengcheng,Sun Guoxiong.Influence of Zr on the Microstructure of Near-Eutectic Al-Si Casting Alloys Modified with Sr[J].Journal of Southeast University (Natural Science Edition),2000,30(6):47-51.[doi:10.3969/j.issn.1001-0505.2000.06.011]
点击复制

Zr对Sr变质近共晶Al-Si铸造合金组织的影响()
分享到:

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
30
期数:
2000年第6期
页码:
47-51
栏目:
材料科学与工程
出版日期:
2000-11-20

文章信息/Info

Title:
Influence of Zr on the Microstructure of Near-Eutectic Al-Si Casting Alloys Modified with Sr
作者:
孙瑜1 廖恒成2 孙国雄2
1 盐城工学院,盐城 224002; 2 东南大学机械工程系, 南京 210096
Author(s):
Sun Yu1 Liao Hengcheng2 Sun Guoxiong2
1 Yancheng Institute of Technology, Yancheng 224002
2 Department of Mechanical Engineering, Southeast University, Nanjing 210096
关键词:
Al-Si合金 锆(Zr) 异质生核
Keywords:
Al-Si alloys Zr hetergeneous nucleation
分类号:
TG146
DOI:
10.3969/j.issn.1001-0505.2000.06.011
摘要:
Sr作为变质剂加入到Al-Si合金中能导致共晶硅的形态从粗大的片状(或针状)转变为细小的纤维状,但同时也促进长柱状枝晶的形成.为了抑制长柱状枝晶的形成,本研究采用金相显微镜和扫描电镜分析Zr对Sr变质近共晶Al-Si铸造合金组织的影响.结果表明,随着Zr加入量的增加,枝晶α(Al)有等轴化趋势,长柱状枝晶的主干长度缩短,且对共晶硅的形态、尺寸没有明显影响,当Zr加入量为0.5%~0.6%时,枝晶α完全等轴化.这是由于熔体中形成了ZrAl3颗粒,在合金凝固过程中,起到了异质生核作用.
Abstract:
The addition of Sr in Al-Si alloys as a modifier can result in transition of eutectic silicon from coarse plate-like or acicular to fine fibrous. However,it may also lead to the formation of long columnar dendrite α phase. The influence of Zr on microstructure of near-eutectic Al-Si alloys was studied using optical microscopy and SEM. The result indicated that increasing of Zr addition, α dendrite tends to change from long columnar to equiaxed, and there were no noticeable changes of the eutectic silicon. When adding 0.5%-0.6%Zr, the dendrite α phase was equiaxed fairly.This is because, during solidification,ZrAl3 particles were formed in the melt playing a role of hetergeneous nucleation.

参考文献/References:

[1] 熊艳才,刘伯操.铸造铝合金现状及未来发展.特种铸造及有色合金,1998(4):1~5
[2] 有色金属及热处理编写组编著.有色金属及热处理.北京:国防工业出版社,1981.1~10
[3] 廖恒成,孙瑜,孙国雄,等.Al-5%-1%B对Sr变质Al-13%Si合金组织的影响的研究.铸造,2000(5):251~256
[4] 余琨,李松瑞,黎文献,等.微量Sc和Zr对2618铝合金再结晶行为的影响.中国有色金属学报,1999(12):699~713
[5] 蒙多尔福L F 著.铝合金的组织与性能.王祝堂,张振录,郑璇,等译.北京:冶金工业出版社,1984.351~353,557
[6] 廖恒成,方信贤,孙国雄.铸造Al-Si合金熔体处理——晶粒细化.特种铸造及有色合金,1999(3):49~537
[7] Mohanty P S,Gruzleski J E.Grain refinement mechanisms of hypoeutectic Al-Si alloys.Acta Mater,1996,44(9):3749~3860
[8] Han S Z,Park S I.Lattice matching of Do23 and Do22 phases in Al-6at.%(Ti,V,Zr) systems.Materials Science and Engineering,1997,230:100~106
[9] Sigworth G H,Guzowki M M.Grain refining of hypo-eutectic Al-Si alloys.AFS Trans,1985,93:907~912

备注/Memo

备注/Memo:
第一作者:男, 1962年生, 硕士研究生, 讲师.
更新日期/Last Update: 2000-11-20