Experimental research on grouting material with large volume fly ash
作者:
童立元 潘石 邱钰 宣国良 刘松玉
东南大学交通学院, 南京 210096
Author(s):
Tong Liyuan Pan Shi Qiu Yu Xuan Guoliang Liu Songyu
Transportation College, Southeast University, Nanjing 210096, China
关键词:
大掺量粉煤灰 注浆充填法 水灰质量比 固相质量比 采空区
Keywords:
large volume fly ash grouting method water cement ratio solid phase proportion mined-out region
分类号:
TU502
DOI:
10.3969/j.issn.1001-0505.2002.04.024
摘要:
为了解大掺量粉煤灰的水泥粉煤灰注浆材料的物理力学性能,通过室内试验,探讨了在大掺量粉煤灰情况下,不同水灰质量比、固相质量比及不同外加剂用量与硬化体抗压强度、浆体凝结时间、流动度、粘度、结石率之间的相互关系.试验表明,随粉煤灰掺量的增加,硬化体抗压强度、浆体流动度降低,而凝结时间延长,结石率和粘度增大; 硬化体早期强度较低,后期强度有较大增长(120 d后仍有所增长); 适量水玻璃的掺入(水玻璃占水泥质量分数不大于3%)使凝结时间缩短,结石率增大,但导致硬化体抗压强度降低,浆体流动性变差; 浆体凝结时间较长,水灰质量比(0.7~1.0):1.0,粉煤灰掺量质量分数为60%~90%时,初凝一般大于12 h,终凝一般大于20 h.
Abstract:
Experiments on cement and fly-ash grouting material with large volume fly-ash were carried out in laboratory in order to understand the correlation between different water cement ratio, solid phase proportion, additive proportion and setting time, viscidity, fluidity, hardening rate, and concretion strength. The results show that with the increase of fly ash proportion the concretion strength and serum fluidity decrease, while setting time, hardening rate and viscidity increase. The early strength of concretion is low while the late strength increases remarkable even after 120 d. With soluble glass mixed(≤3%), setting time decreases and hardening rate increases,but at the same time the concretion strength and fluidity decrease. The setting time is quite long, when the water cement ratio is(0.7-1.0):1 and the proportion of fly ash is 60%-90%, the early setting time is longer than 12 hours and the last setting time is longer than 20 hours.

参考文献/References:

[1] 杜广印,童立元,刘松玉.高速公路下伏多层煤矿采空区处治方法研究[J].东南大学学报(自然科学版),2001,31(3A):115-118.
  Du Guangyin,Tong Liyuan,Liu songyu.Methods of treating multi-layer mined-out areas under expressway[J].Journal of Southeast University(Nature Science Edition),2001,31(3A):115-118.(in Chinese)
[2] 张志沛.高速公路煤矿采空区地基注浆加固治理技术[J].中南公路工程,1996(1):23-28.
  Zhang Zhipei.The grouting technical treating coal mined-out region under expressway[J].Middle-South Highway Engineering,1996(1):23-28.(in Chinese)
[3] 地基处理手册编委会.地基处理手册[S].北京:中国建筑工业出版社,1994.263-264.
  Manual committee Ground improvement manual[S].Beijing:China Architecture and Building Press,1994.263-264.(in Chinese)
[4] 蒋天华.水泥粉煤灰灌浆的探索与应用[J].浙江水利水电专科学校学报,2000(1):37-38.
  Jiang Tianhua.Research and application of cement and fly ash grouting[J].Journal of Zhejiang Wat Cons & Hydr College,2000(1):37-38.(in Chinese)
[5] 樊天龙.冶勒大坝基础灌浆浆材试验探讨[J].四川水力发电,1995(4):46-53.
  Fan Tianlong.Study on grouting agent test in foundation grouting at Yeile Dam in Nanya River[J].Szechuan Waterpower,1995(4):46-53.(in Chinese)
[6] 杨锡武.粉煤灰水化过程模型的研究[J].中国公路学报,1994,7(1):61-66.
  Yang Xiwu.On the hydration process model of pulverized fly ash[J].China Journal of Highway and Transport,1994,7(1):61-66.(in Chinese)
[7] 潘钢华,王爱勤.改善粉煤灰水泥早期性能的两个措施[J].东南大学学报,1998,28(1):97-102.
  Pan Ganghua,Wang Aiqin.Measures for improving the properties of fly ash cement[J].Journal of Southeast University,1998,28(1):97-102.(in Chinese)

备注/Memo

备注/Memo:
作者简介: 童立元(1975—),男,博士生; 刘松玉(联系人),男,博士,教授,博士生导师.
更新日期/Last Update: 2002-07-20