[1]王立燕,王超,张亚梅,等.运用声发射技术研究橡胶混凝土疲劳损伤过程[J].东南大学学报(自然科学版),2009,39(3):574-579.[doi:10.3969/j.issn.1001-0505.2009.03.029]
 Wang Liyan,Wang Chao,Zhang Yamei,et al.Study on fatigue damage process of rubberized cement concrete by acoustic emission technique[J].Journal of Southeast University (Natural Science Edition),2009,39(3):574-579.[doi:10.3969/j.issn.1001-0505.2009.03.029]
点击复制

运用声发射技术研究橡胶混凝土疲劳损伤过程()
分享到:

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
39
期数:
2009年第3期
页码:
574-579
栏目:
材料科学与工程
出版日期:
2009-05-20

文章信息/Info

Title:
Study on fatigue damage process of rubberized cement concrete by acoustic emission technique
作者:
王立燕1 王超2 张亚梅1 马爱斌2
1 东南大学江苏省土木工程材料重点实验室, 南京 211189; 2 河海大学材料科学与工程学院, 南京 210098
Author(s):
Wang Liyan1 Wang Chao2 Zhang Yamei1 Ma Aibin2
1 Jiangsu Key Laboratory of Construction Materials, Southeast University,Nanjing 211189,China
2 College of Materials Science and Engineering,Hohai University, Nanjing 210098,China
关键词:
橡胶混凝土 声发射 疲劳损伤
Keywords:
rubberized cement concrete acoustic emission fatigue damage
分类号:
TU528.01
DOI:
10.3969/j.issn.1001-0505.2009.03.029
摘要:
借助声发射技术对水泥混凝土及橡胶水泥混凝土的疲劳过程进行实时监测,通过声发射信号的强度和活度等相关参数分析疲劳损伤过程.实验结果表明:疲劳循环加载过程中,0.6,0.7,0.8应力水平下水泥混凝土中声发射信号的撞击总数随时间变化均呈现近似线性增长趋势,幅度随时间变化分布密集,声发射信号连续发生,表明水泥混凝土的疲劳损伤过程是一个持续的损伤累计增长的过程; 橡胶混凝土声发射信号的撞击总数随时间变化曲线分为中间阶段曲线平缓、幅度随时间变化分布松散3个阶段,疲劳损伤全过程呈现典型的裂纹引发、稳定扩展和失稳扩展3个阶段.由于在疲劳循环加载过程中橡胶的能量耗散特性以及良好的吸声性能,橡胶混凝土中声发射信号发生的强度和活度普遍低于同应力水平下的普通水泥混凝土,损伤演化速度缓慢,损伤程度降低,因此具有优异的疲劳性能.
Abstract:
An acoustic emission(AE)technique is used to monitor the fatigue process of common cement concrete and rubberized cement concrete. The fatigue damage process is analyzed through AE parameters of activity and intensity. The experimental results show that, at each stress level, the accumulative hits of common cement concrete rise almost linearly with loading time under cyclic loading, and AE signals are continuous during the whole fatigue process, which demonstrates the continuous damage accumulation inside common cement concrete. However, the accumulative hits of rubberized cement concrete develop in a different manner. The curves of AE parameters are characterized by three typical damage stages, i.e., initiation of cracks, stable propagation and unstable propagation of cracks. At the stable propagation stage, the distribution of AE signals with loading time is loose. Due to the energy dissipation effect and the acoustic adsorption of elastic rubber particles, both the activity and intensity of AE signals in rubberized cement concrete are lower than in common cement concrete, therefore less damage is detected and better fatigue performance is achieved in rubberized cement concrete.

参考文献/References:

[1] Labuz Joseph F,Cattaneo Sara,Chen Li-Hsien.Acoustic emission at failure in quasi-brittle materials[J].Construction and Building Materials,2001,15(5/6):225-233.
[2] Lee Jin-Kyung,Lee Joon-Hyun.Nondestructive evaluation on damage of carbon fiber sheet reinforced concrete[J].Composite Structures,2002,58(1):139-147.
[3] Sagaidak A I,Elizarov S V.Acoustic emission parameters correlated with fracture and deformation processes of concrete members[J]. Construction and Building Materials,2007,21(3):477-482.
[4] Elaqra H,Godin N,Peix G,et al.Damage evolution analysis in mortar,during compressive loading using acoustic emission and X-ray tomography:effects of the sand/cement ratio[J]. Cement and Concrete Research,2007,37(5):703-713.
[5] 陈兵,姚武,张东,等.混凝土梁破坏机制的声发射特性实验研究[J].建筑材料学报,2001,4(4):332-338.
  Chen Bing,Yao Wu,Zhang Dong,et al.Study on the AE characteristics of fracture process of concrete beams[J].Journal of Building Materials,2001,4(4):332-338.(in Chinese)
[6] 朱宏平,徐文胜,陈晓强,等.利用声发射信号与速率过程理论对混凝土损伤进行定量评估[J].工程力学,2008,25(1):186-191.
  Zhu Hongping,Xu Wensheng,Chen Xiaoqiang,et al.Quantitative concrete-damage evaluation by acoustic emission information and rate-process theory[J].Engineering Mechanics,2008,25(1):186-191.(in Chinese)
[7] 纪洪广,张天森,蔡美峰,等.混凝土材料损伤的声发射动态检测试验研究[J].岩石力学与工程学报,2000,19(2):165-168.
  Ji Hongguang,Zhang Tiansen,Cai Meifeng,et al.Experimental study on concrete damage by dynamic measurement of acoustic emission[J].Chinese Journal of Rock Mechanics and Engineering,2000,19(2):165-168.(in Chinese)
[8] Shigeishi Mitsuhiro,Ohtsu Masayasu.Acoustic emission moment tensor analysis:development for crack identification in concrete materials[J].Construction and Building Materials,2001,15(5/6):311-319.
[9] Grosse Christian U,Finck Florian.Quantitative evaluation of fracture processes in concrete using signal-based acoustic emission techniques[J].Cement & Concrete Composites,2006,28(4):330-336.
[10] Yuyama S,Li Z W,Yoshizawa M,et al.Evaluation of fatigue damage in reinforced concrete slab by acoustic emission[J].NDT& E International,2001,34(6):381-387.
[11] Thummen F,Olagnon C,Godin N.Cyclic fatigue and lifetime of a concrete refractory[J].Journal of the European Ceramic Society,2006,26(15):3357-3363.
[12] Eldin N N,Senouci A B.Rubber-tire practices as concrete aggregate[J].Mater Cic Eng,1993,5(4):478-496.
[13] Li Guoqiang,Garrick Gregory,Eggers John.Waste tire fiber modified concrete[J].Composites:Part B,2004,35(4):305-312.
[14] 熊杰,郑磊,袁勇.废橡胶混凝土抗压强度试验研究[J].混凝土,2004(12):40-42.
  Xiong Jie,Zheng Lei,Yuan Yong.Experimental study on compressive strength of rubberized concrete[J].Concrete,2004(12):40-42.(in Chinese)
[15] 朱涵,刘春生,张永明,等.橡胶集料掺量对混凝土压弯性能的影响[J].天津大学学报,2007,40(7):763-764.
  Zhu Han,Liu Chunsheng,Zhang Yongming,et al.Effect of crumb rubber proportion on compressive and flexural behavior of concrete[J].Journal of Tianjin University,2007,40(7):763-764.(in Chinese)
[16] 欧兴进,朱涵.橡胶集料混凝土氯离子渗透性试验研究[J].混凝土,2006(3):46-49.
  Ou Xingjin,Zhu Han.Experimental study on chloride ion permeability of crumb rubber concrete[J].Concrete,2006(3):46-49.(in Chinese)
[17] 陈波,张亚梅,陈胜霞.橡胶混凝土性能的初步研究[J].混凝土,2004(12):37-39.
  Chen Bo,Zhang Yamei,Chen Shengxia.Fundamental research of properties of rubberized concretes[J].Concrete,2004(12):37-39.(in Chinese)
[18] 陈胜霞.橡胶改性水泥基材料的耐久性研究[D].南京:东南大学材料科学与工程学院,2004.
[19] 刘春生,朱涵,李志国,等.橡胶细集料水泥砂浆基本性能研究[J].混凝土,2005(7):38-42.
  Liu Chunsheng,Zhu Han,Li Zhiguo,et al.Research in the fundamental characteristics of crumb rubber mortar[J].Concrete,2005(7):38-42.(in Chinese)
[20] 亢景付,任海波,张平祖.橡胶混凝土的抗裂性能和弯曲变形性能[J].复合材料学报,2006,23(6):158-162.
  Kang Jingfu,Ren Haibo,Zhang Pingzu.Cracking-resistance and flexural property of rubberized concrete[J].Acta Materiae Compositae Sinica,2006,23(6):158-162.(in Chinese)
[21] 赵志远,毕乾,王立燕,等.废橡胶颗粒改性水泥基材料的塑性开裂和抗冲击性能[J].混凝土与水泥制品,2008(4):1-5.
  Zhao Zhiyuan,Bi Qian,Wang Liyan,et al.Plastical cracking and resistance to impact for rubber particle modified cement-based composites[J].China Concrete and Cement Products,2008(4):1-5.(in Chinese)
[22] 陈振富,柯国军,胡绍全,等.橡胶混凝土小变形阻尼研究[J].噪声与振动控制,2004(3):32-34.
  Chen Zhenfu,Ke Guojun,Hu Shaoquan,et al.Study on damping of rubber powder concrete in small deformation[J].Noise and Vibration Control,2004(3):32-34.(in Chinese)
[23] 许静,朱涵,刘春生,等.橡胶集料混凝土阻尼比的初步试验研究[J].混凝土,2005(11):40-42.
  Xu Jing,Zhu Han,Liu Chunsheng,et al.Preliminary experimental studies on damping ratio of crumb rubber concrete[J].Concrete,2005(11):40-42.(in Chinese)
[24] Herna’ndez-Olivares F,Barluenga G,Parga-Landa B,et al.Fatigue behaviour of recycled tyre rubber-filled concrete andits implications in the design of rigid pavements[J]. Construction and Building Materials,2007,21(10):1918-1927.
[25] 刘乃亮,齐暑华,周文英,等.吸声功能橡胶研究进展[J].特种橡胶制品,2008,29(4):45-50.
  Liu Nailiang,Qi Shuhua,Zhou Wenying,et al.Progress in research of sound absorption functional rubber[J].Special Purpose Rubber Products,2008,29(4):45-50.(in Chinese)
[26] 陈兵,吕子义,周钟鸣.水泥基复合材料微结构破坏声发射研究[J].无损检测,2004,26(4):184-187.
  Chen Bing,Lü Ziyi,Zhou Zhongming.Study on microstructure fracture of cement-based composites by acoustic emission technique[J].Nondestructive Testing,2004,26(4):184-187.(in Chinese)

相似文献/References:

[1]邓艾东,童航,张如洋,等.基于模态分析的转子碰摩声发射特征[J].东南大学学报(自然科学版),2010,40(6):1232.[doi:10.3969/j.issn.1001-0505.2010.06.020]
 Deng Aidong,Tong Hang,Zhang Ruyang,et al.Characteristics of rub-impact AE signals in rotating machinery based on modal analysis[J].Journal of Southeast University (Natural Science Edition),2010,40(3):1232.[doi:10.3969/j.issn.1001-0505.2010.06.020]
[2]李杰.混凝土随机损伤本构关系研究新进展[J].东南大学学报(自然科学版),2002,32(5):750.[doi:10.3969/j.issn.1001-0505.2002.05.016]
 Li Jie.Recent research progress on the stochastic damage constitutional law of concrete[J].Journal of Southeast University (Natural Science Edition),2002,32(3):750.[doi:10.3969/j.issn.1001-0505.2002.05.016]
[3]无线电工程系水声仿生课题组.生物透声窗——白暨豚额隆声学特性测量[J].东南大学学报(自然科学版),1980,10(2):121.[doi:10.3969/j.issn.1001-0505.1980.02.013]
 The Research Team of Underwater Acoustic Bionics..Animal Transmissive Window——Acoustic Measurement of the Melon of Lipotes Vexillifer[J].Journal of Southeast University (Natural Science Edition),1980,10(3):121.[doi:10.3969/j.issn.1001-0505.1980.02.013]

备注/Memo

备注/Memo:
作者简介: 王立燕(1982—),女,硕士生; 张亚梅(联系人),女,博士,教授,博士生导师,ymzhang@seu.edu.cn.
基金项目: 国家自然科学基金资助项目(50778039)、江苏省自然科学基金资助项目(BK2007111).
引文格式: 王立燕,王超,张亚梅,等.运用声发射技术研究橡胶混凝土疲劳损伤过程[J].东南大学学报:自然科学版,2009,39(3):574-579. [doi:10.3969/j.issn.1001-0505.2009.03.029]