[1]孙复钱,姚琛,李新松,等.电纺聚-L-乳酸/β-磷酸三钙复合物纳米纤维膜[J].东南大学学报(自然科学版),2010,40(1):213-217.[doi:10.3969/j.issn.1001-0505.2010.01.040]
　Sun Fuqian,Yao Chen,Li Xinsong,et al.Electrospun poly-L-lactic acid/β-tricalcium phosphate composite nanofiber membranes[J].Journal of Southeast University (Natural Science Edition),2010,40(1):213-217.[doi:10.3969/j.issn.1001-0505.2010.01.040]
点击复制

电纺聚-L-乳酸/β-磷酸三钙复合物纳米纤维膜()
分享到：

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
40
期数:
2010年第1期
页码:
213-217
栏目:
化学化工
出版日期:
2010-01-20

文章信息/Info

Title:
Electrospun poly-L-lactic acid/β-tricalcium phosphate composite nanofiber membranes
作者:
孙复钱1;  姚琛1;  李新松1;  范凯红2;  浦跃朴2
1 东南大学化学化工学院,南京 210018; 2 东南大学公共卫生学院, 南京 210018
Author(s):
Sun Fuqian1;  Yao Chen1;  Li Xinsong1;  Fan Kaihong2;  Pu Yuepu2
1 School of Chemistry and Chemical Engineering, Southeast University, Nanjing 210018,China
2 School of Public Health, Southeast University, Nanjing 210018,China
关键词:
电纺;  纳米纤维膜;  聚-L-乳酸;  β-磷酸三钙;  复合物
Keywords:
electrospinning;  nanofiber membrane;  poly-L-lactic acid;  β-tricalcium phosphate;  composite
分类号:
TQ342.94
DOI:
10.3969/j.issn.1001-0505.2010.01.040
摘要:
利用静电纺丝法制备了生物可吸收聚-L-乳酸(PLLA)/β-磷酸三钙(β-TCP)复合物纳米纤维膜.采用扫描电子显微镜(SEM)、场发射扫描电子显微镜(FESEM)等手段研究了复合物纳米纤维膜的结构和形态,详细探讨电纺工艺条件对制备PLLA/β-TCP复合物纳米纤维的形态影响.通过拉伸力学测试、噻唑蓝比色法(MTT)对复合物纳米纤维膜的力学性能和体外细胞相容性作了进一步研究.结果表明,PLLA/β-TCP复合物纳米纤维的几何结构与电纺条件有关,随着聚合物溶液浓度增加、溶液流速增大,纤维直径有不同程度的增大; 复合物纳米纤维膜的拉伸强度和杨氏模量随β-TCP的含量增加而下降; 复合物纳米纤维膜对L-929细胞系无细胞毒性,显示良好的细胞相容性.
Abstract:
Poly(L-lactic acid)/β-tricalcium phosphate(PLLA/β-TCP)composite nanofiber membranes were prepared by electrospinning.The structure and morphology of the composite nanofiber membranes were studied by scanning electron microscopy(SEM)and field emission scanning electron microscopy(FESEM). And mechanical properties of composite nanofiber membranes were characterized by tensile tester. A primary study of the cellular compatibility of the composite nanofiber membranes was carried out by MTT(methylthiazolyldiphenyl-tetrazolium bromide)assay. The results show that the geometrical structures of the composite nanofibers depend on processing parameters such as PLLA concentration. With the increasing of PLLA concentration and feed rate, the diameters of the fibers increase. The tensile strength and Young’s modulus of composite nanofiber membranes are lowered with increasing the content of β-TCP. Electrospun PLLA/β-TCP composite nanofibers show good cytocompatibility to L-929 cells according to MTT assay.

参考文献/References:

[1] Yoon K,Kim K,Wang X F,et al.High flux ultrafiltration membranes based on electrospun nanofibrous PAN scaffolds and chitosan coating[J].Polymer,2006,47(5):2434-2441.
[2] Kumbar S G,Nukavarapu S P,James R,et al.Electrospun poly(lactic acid-co-glycolic acid)scaffolds for skin tissue engineering[J].Biomaterials,2008,29(13):4100-4107.
[3] Sombatmankhong K,Sanchavanakit N,Pavasant P,et al.Bone scaffolds from electrospun fiber mats of poly(3-hydroxybutyrate),poly(3-hydroxybutyrate-co-3-hydroxyvalerate)and their blend[J]. Polymer,2007,48(5):1419-1427.
[4] Im J S,Kim M I,Lee Y S.Preparation of PAN-based electrospun nanofiber webs containing TiO2 for photocatalytic degradation[J].Materials Letters,2008,62(21/22):3652-3655.
[5] Saeed K,Park S Y,Lee H J,et al.Preparation of electrospun nanofibers of carbon nanotube/polycaprolactone nanocomposite[J]. Polymer,2006,47(23):8019-8025.
[6] Cai Q,Yang J,Bei J,et al.A novel porous cells scaffold made of polylactide-dextran blend by combining phase-separation and particle-leaching techniques[J]. Biomaterials,2002,23(23):4483-4492.
[7] Aussawasathien D,Teerawattananon C,Vongachariya A.Separation of micron to sub-micron particles from water:electrospun nylon-6 nanofibrous membranes as pre-filters[J].Journal of Membrane Science,2008,315(1/2):11-19.
[8] Benjamin C,Benjamin S H,Dufei F,et al.Biodegradable and/or bioabsorbable fibrous articles and methods for using the articles in medical applications:US,0173213[P].2002-11-21.
[9] Mo X M,Xu C Y,Kotaki M,et al.Electrospun P(LLA-CL)nanofiber:a biomimetic extracellular matrix for smooth muscle cell and endothelial cell proliferation[J]. Biomaterials,2004,25(10):1883-1890.
[10] Swieszkowski W,Tuan B H S,Kurzydlowski K J,et al.Repair and regeneration of osteochondral defects in the articular joints[J].Biomolecular Engineering,2007,24(5):489-495.
[11] Gilding D K,Reed A M.Biodegradable polymers for use in surgery polyglycolic/poly(actic acid)homo and copolymers:1[J]. Polymer,1979,20(12):1459-1464.
[12] Yeong K C B,Wang J,Ng S C.Fabricating desified hydroxyapatite ceramice fron a precipitated precursor[J].Materials Letter,1999,38(3):208-213.
[13] Fong H,Chun I,Reneker D H.Beaded nanofibers formed during electrospinning[J].Polymer,1999,40(16):4585-4592.
[14] Xinhua Z,Kwangsok K,Dufei F,et al.Structure and process relationship of electrospun bioabsorbable nanofiber membranes[J].Polymer,2002,43(16):4403-4412.

备注/Memo

备注/Memo:
作者简介: 孙复钱(1981—),男,博士生; 李新松(联系人),男,博士,教授,博士生导师,lixs@seu.edu.cn.
基金项目: 国家自然科学基金资助项目(50673019).
引文格式: 孙复钱,姚琛,李新松,等.电纺聚-L-乳酸/β-磷酸三钙复合物纳米纤维膜[J].东南大学学报:自然科学版,2010,40(1):213-217. [doi:10.3969/j.issn.1001-0505.2010.01.040]
更新日期/Last Update: 2010-01-20