[1]王晓波,王芳,姚桂焕,等.Zr-Mn-Fe/Al2O3的低温脱硝性能[J].东南大学学报(自然科学版),2010,40(2):388-392.[doi:10.3969/j.issn.1001-0505.2010.02.033]
　Wang Xiaobo,Wang Fang,Yao Guihuan,et al.Performance of low temperature De-NOx based on Zr-Mn-Fe/Al2O3[J].Journal of Southeast University (Natural Science Edition),2010,40(2):388-392.[doi:10.3969/j.issn.1001-0505.2010.02.033]
点击复制

Zr-Mn-Fe/Al2O3的低温脱硝性能()
分享到：

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
40
期数:
2010年第2期
页码:
388-392
栏目:
环境科学与工程
出版日期:
2010-03-20

文章信息/Info

Title:
Performance of low temperature De-NOx based on Zr-Mn-Fe/Al2O3
作者:
王晓波;  王芳;  姚桂焕;  归柯庭
东南大学能源与环境学院, 南京 210096
Author(s):
Wang Xiaobo;  Wang Fang;  Yao Guihuan;  Gui Keting
School of Energy and Environment, Southeast University, Nanjing 210096, China
关键词:
低温脱硝;  脱除率;  Zr-Mn-Fe/Al2O3
Keywords:
low-temperature de-NOx;  removal efficiency;  Zr-Mn-Fe/Al2O3
分类号:
X5
DOI:
10.3969/j.issn.1001-0505.2010.02.033
摘要:
采用浸渍法用ZrOCl2·8H2O,Mn(NO3)2·6H2O和Fe(NO3)3·9H2O制备了Zr-Mn-Fe/Al2O3复合催化剂.通过调节质量分数分别为2%,5%和10%金属元素锰和锆的负载量制备了不同的催化剂,测试了其在NH3条件下的低温脱硝活性,研究了不同组分配比和氧气含量对催化剂脱硝性能的影响.通过在载体上分别单独负载Mn,Fe和Zr来探究脱硝过程中起主要作用的催化活性组分.实验结果表明,在体积分数φ(NO)=0.05%,摩尔比n(NH3):n(NO)=1:1和φ(O2)=3.6%的条件下,制备的催化剂5Zr-5Mn-10Fe/Al2O3表现出很高的催化活性,在180 ℃时脱除效率超过了98%,是一种良好的低温SCR催化剂. Mn在脱硝过程中是主要的活性组分,而Zr和Fe是助催化组分.此外,在反应过程中通入一定的氧气,可以明显提高NO的脱除效率,能促进NO的转化.
Abstract:
Zr-Mn-Fe/Al2O3 catalysts were prepared by a simple impregnation method using ZrOCl2·8H2O,Mn(NO3)2·6H2O and Fe(NO3)3·9H2O on the Al2O3 carrier. The weight fractions of loading Mn and Zr on the catalysts were individually adjusted with 2%, 5%, and 10%. These catalysts were used to investigate low temperature selective catalytic reduction of NO with ammonia. The influences of metal loading and O2on the de-NOx efficiency were also studied. Mn, Fe and Zr were individually loaded on Al2O3to ascertain the main catalytic activity component. Results show that the catalyst of 5Zr-5Mn-10Fe/Al2O3 is of higher de-NOx efficiency in the simulated flue gas of 0.05% NO with a 1:1 NH3/NO molar ratio in the presence of a volume fraction of 3.6% O2. This catalyst yields 98% NO conversion at 180 ℃ under the mentioned conditions and is a type of good low temperature selective catalytic reduction(SCR)catalyst. Mn is the main acting component in the process of NO removal in this catalyst, while the Zr and Fe are acting as a promoter. In addition, oxygen can significantly improve the efficiency of NO removal.

参考文献/References:

[1] 朱崇兵,金保升,仲兆平,等.K2O对V2O5-WO3/TiO2催化剂的中毒作用[J].东南大学学报:自然科学版,2008,38(1):101-105.
　　Zhu Chongbing,Jin Baosheng,Zhong Zhaoping,et al.Poisoning effect of K2O on V2O5-WO3/TiO2 catalysts[J].Journal of Southeast University:Natural Science Edition,2008,38(1):101-105.(in Chinese)
[2] 沈伯雄,史展亮,施建伟,等.基于Mn-CeOx/ACFN的低温SCR脱硝[J].化工进展,2008,27(1):87-91.
　 Shen Boxiong,Shi Zhanliang,Shi Jianwei,et al.Research on de-NO by low-temperature SCR based on Mn-CeOx/ACFN[J].Chemical Industry and Engineering Progress,2008,27(1):87-91.(in Chinese)
[3] 吴碧君,刘晓勤,肖萍,等.Mn-Fe/TiO2低温NH3选择性还原NO催化活性及其反应机制[J].中国电机工程学报,2007,27(17):51-56.
　 Wu Bijun,Liu Xiaoqin,Xiao Ping,et al.Catalytic performance and mechanism of Mn-Fe/TiO2for low-temperature selective reduction of NO with NH3[J].Proceedings of the CSEE,2007,27(17):51-56.(in Chinese)
[4] 寻洲,童华,黄妍,等.Mn-Ce-Fe/TiO2低温催化还原NO的性能[J].环境科学报,2008,28(9):1733-1738.
　 Xun Zhou,Tong Hua,Huang Yan,et al.Reduction of NO with Mn-Ce-Fe/TiO2 as catalyst at low temperature[J].Acta Scientiae Circumstantiae,2008,28(9):1733-1738.(in Chinese)
[5] 赵清森,孙路石,向军,等.CuO/γ-Al2O3和CuO-CeO2-Na2O/γ-Al2O3催化吸附剂的脱硝性能[J].中国电机工程报,2008,28(8):52-57.
　 Zhao Qinsen,Sun Lushi,Xiang Jun,et al.Selective catalytic reduction of NO over CuO/γ-Al2O3 and CuO-CeO2-Na2O/γ-Al2O3 catalysts[J].Proceedings of the CSEE,2008,28(8):52-57.(in Chinese)
[6] Kang M,Park E D,Kim J M,et al.Cu-Mn mixed oxides for low temperature NO reduction with NH3[J].Catalysis Today,2006,111(3/4):236-241.
[7] Qi G,Yang R T.Low-temperature selective catalytic reduction of NO with NH3 over iron and manganese oxides supported on titania [J]. Applied Catalysis B:Environmental,2003,44(3):217-225.
[8] Apostolescu N,Geiger B,Hizbullah K,et al.Selective catalytic reduction of nitrogen oxides by ammonia on iron oxide catalysts[J].Applied Catalysis B:Environmental,2006,62(1/2):104-114.
[9] Huang J,Tong Z,Huang Y,et al.Selective catalytic reduction of NO with NH3 at low temperatures over iron and manganese oxides supported on mesoporous silica[J].Applied Catalysis B:Environmental,2008,78(3/4):309-314.
[10] Qi G,Yang R T.Ultra-active Fe/ZSM-5 catalyst for selective catalytic reduction of nitric oxide with ammonia[J].Applied Catalysis B:Environmental,2005,60(1/2):13-22.

备注/Memo

备注/Memo:
作者简介: 王晓波(1982—),男,博士生; 归柯庭(联系人),男,博士,教授,博士生导师,ktgui@seu.edu.cn.
基金项目: 国家自然科学基金资助项目(50576013).
引文格式: 王晓波,王芳,姚桂焕,等.Zr-Mn-Fe/Al2O3的低温脱硝性能[J].东南大学学报:自然科学版,2010,40(2):388-392. [doi:10.3969/j.issn.1001-0505.2010.02.033]
更新日期/Last Update: 2010-03-20