[1]刘加平,王育江,田倩,等.轻烧氧化镁膨胀剂膨胀性能的温度敏感性及其机理分析[J].东南大学学报(自然科学版),2011,41(2):359-364.[doi:10.3969/j.issn.1001-0505.2011.02.028]
 Liu Jiaping,Wang Yujiang,Tian Qian,et al.Temperature sensitivity of light calcined magnesia expansion agent and its mechanism analysis[J].Journal of Southeast University (Natural Science Edition),2011,41(2):359-364.[doi:10.3969/j.issn.1001-0505.2011.02.028]
点击复制

轻烧氧化镁膨胀剂膨胀性能的温度敏感性及其机理分析()
分享到:

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
41
期数:
2011年第2期
页码:
359-364
栏目:
材料科学与工程
出版日期:
2011-03-20

文章信息/Info

Title:
Temperature sensitivity of light calcined magnesia expansion agent and its mechanism analysis
作者:
刘加平王育江田倩张守治
(江苏省建筑科学研究院有限公司高性能土木工程材料国家重点实验室, 南京211103)
Author(s):
Liu JiapingWang YujiangTian QianZhang Shouzhi
(State Key Laboratory of High Performance Civil Engineering Materials, Jiangsu Academy of Building Science, Co., Ltd.,Nanjing 211103, China)
关键词:
氧化镁膨胀剂水化动力学水化活性温度敏感性
Keywords:
MgO-type expansion agent hydration kinetics hydration activity temperature sensitivity
分类号:
TU528.01
DOI:
10.3969/j.issn.1001-0505.2011.02.028
摘要:
为了考察温度对轻烧氧化镁膨胀剂膨胀性能的影响,选取了2种典型煅烧活性的轻烧氧化镁,研究了氧化镁水化速率及掺加氧化镁浆体变形性能的温度敏感性,并从氧化镁水化动力学角度对其机理进行分析.试验结果表明:低活性轻烧氧化镁的水化及膨胀速率显著依赖反应温度,表现出较强的温度敏感性; 轻烧氧化镁的水化过程同样可以划分为和硅酸盐水泥相近的5个阶段,试验所采用的2种氧化镁在水化反应诱导期及加速期的活化能(分别为75.9和149.8 kJ/mol)差异最为显著.氧化镁膨胀剂自身膨胀效能及水化反应动力学参数的差异是造成温度敏感性差异的主要原因.
Abstract:
To evaluate the effect of temperature on expansion of light calcined magnesia expansion agent (MEA), two typical MEA were chosen, and temperature sensitivity of hydration rate of MEA and expansive process of cement paste containing MEA were analyzed. Furthermore, the mechanism of temperature was also discussed based on hydration kinetics of MEA. The results indicate that the hydration and expansion of MEA calcined at higher temperature show stronger temperature sensitivity compared to that calcined at lower temperature. Similar to Portland cement, the hydration process of MEA can also be divided into five stages, and the activation energy difference in induction and acceleration period of hydration reaction is remarkable (75. 9 and 149. 8 kJ/mol, for two MEA respectively). The differences of expansive effectiveness and kinetic parameters are the main cause of the difference of temperature sensitivity.

参考文献/References:

[1] 李红,邓敏,莫立武.不同活性氧化镁膨胀剂对水泥浆体变形的影响[J].南京工业大学学报:自然科学版,2010,32(6):98-102.
  Li Hong,Deng Min,Mo Liwu.Influence of MgO-bearing expansive agent in different activities on deformation of cement pasetes[J].Journal of Nanjing University of Technology:Natural Science Edition,2010,32(6):98-102.(in Chinese)
[2] 徐玲玲,邓敏,赵霞.新型镁质膨胀材料对水泥浆体收缩的补偿[J].建筑材料学报,2005,8(1):67-70.
  Xu Lingling,Deng Min,Zhao Xia.Compensating shrinkage of cement paste by new MgO-based expansive material[J].Journal of Building Materials,2005,8(1):67-70.(in Chinese)
[3] 田倩,涂扬举,刘加平,等.氧化镁复合膨胀剂膨胀性能的温度敏感性研究[J].水力发电,2010,36(6):49-51.
  Tian Qian,Tu Yangju,Liu Jiaping,et al.Temperature sensitivity analysis on expansion property of MgO composite expansion agent[J].Water Power,2010,36(6):49-51.(in Chinese)
[4] Kitamura A,Ishikawa M,Onizuka K,et al.Hydration of magnesia clinkers[J].Refractories(Tokyo),1994,46(11):599.
[5] Birchal V S,Rocha S D F,Mansur M B,et al.A simplified mechanistic analysis of the hydration of magnesia[J].The Canadian Journal of Chemical Engineering,2001,79(4):507-511.
[6] 钱海燕,李素英,邓敏,等.轻烧氧化镁水化动力学[J].化学矿物与加工,2007(12):1-4.
  Qian Haiyan,Li Suying,Deng Min,et al.Hydration dynamic of light-burned magnesia[J].Industrial Minerals &Processing,2007(12):1-4.(in Chinese)
[7] Salomo Rafael,Bittencourt L R M,Pandolfelli V C.A novel approach for magnesia hydration assessment in refractory castables[J].Ceramics International,2007,33(5):803-810.
[8] 刘飚,翟国芳,李仕群,等.硅酸盐与磷铝酸盐复合水泥水化动力学的研究[J].建筑材料学报,2008,11(3):259-265.
  Liu Biao,Zhai Guofang,Li Shiqun,et al.Research on hydration kinetics of composite cement of phosphoaluminate and silicate[J].Journal of Building Materials,2008,11(3):259-265.(in Chinese)
[9] Krstulovic R,Dabic P.A conceptual model of the cement hydration process[J].Cement and Concrete Research,2000,30(5):693-698.
[10] Knudsen T.On particle size distribution in cement hydration[C]//Proceedings of 7th International Congress on the Chemistry of Cement.Paris,France,1980:170-175.
[11] 邓敏,崔雪华,刘元湛,等.水泥中氧化镁的膨胀机理[J].南京化工学院学报,1990,12(4):1-10.
  Deng Min,Cui Xuehua,Liu Yuanzhan,et al.Expansive mechanism of magnesia as an additive of cement[J].Journal of NanJing Institute of Chemical Technology,1990,12(4):1-10.(in Chinese)
[12] Mo Liwu,Deng Min,Tang Mingshu.Effects of calcination condition on expansion property of MgO-type expansive agent used in cement-based materials[J].Cement and Concrete Research,2010,40(3):437-446.

相似文献/References:

[1]曹园章,郭丽萍,薛晓丽.NaCl和Na2SO4对水泥水化机理的影响[J].东南大学学报(自然科学版),2019,49(4):712.[doi:10.3969/j.issn.1001-0505.2019.04.014]
 Cao Yuanzhang,Guo Liping,Xue Xiaoli.Effects of sodium chloride and sodium sulfate on hydration process[J].Journal of Southeast University (Natural Science Edition),2019,49(2):712.[doi:10.3969/j.issn.1001-0505.2019.04.014]

备注/Memo

备注/Memo:
作者简介:刘加平(1967—),男,博士,教授级高级工程师,ljp@cnjsjk.cn.
基金项目:国家重点基础研究发展计划(973计划)资助项目(2010CB735801).
引文格式: 刘加平,王育江,田倩,等.轻烧氧化镁膨胀剂膨胀性能的温度敏感性及其机理分析[J].东南大学学报:自然科学版,2011,41(2):359-364.[doi:10.3969/j.issn.1001-0505.2011.02.028]
更新日期/Last Update: 2011-03-20