[1]余振新,高建明,宋鲁光,等.荷载-干湿交替-硫酸盐耦合作用下混凝土损伤过程[J].东南大学学报(自然科学版),2012,42(3):487-491.[doi:10.3969/j.issn.1001-0505.2012.03.018]
 Yu Zhenxin,Gao Jianming,Song Luguang,et al.Damage process of concrete exposed to sulfate attack under drying-wetting cycles and loading[J].Journal of Southeast University (Natural Science Edition),2012,42(3):487-491.[doi:10.3969/j.issn.1001-0505.2012.03.018]
点击复制

荷载-干湿交替-硫酸盐耦合作用下混凝土损伤过程()
分享到:

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
42
期数:
2012年第3期
页码:
487-491
栏目:
材料科学与工程
出版日期:
2012-05-20

文章信息/Info

Title:
Damage process of concrete exposed to sulfate attack under drying-wetting cycles and loading
作者:
余振新 高建明 宋鲁光 汪廷秀 薛宝法 孙伟
东南大学江苏省土木工程材料重点实验室, 南京 211189
Author(s):
Yu Zhenxin Gao Jianming Song Luguang Wang Tingxiu Xue Baofa Sun Wei
Jiangsu Key Laboratory of Construction Materials, Southeast University, Nanjing 211189, China
关键词:
弯曲荷载 干湿交替 硫酸盐 耦合作用 微观结构
Keywords:
flexural loading drying-wetting cycles sulfate coupling effect microstructure
分类号:
TU528
DOI:
10.3969/j.issn.1001-0505.2012.03.018
摘要:
研究了弯曲荷载-干湿交替-硫酸盐三因素耦合作用下的混凝土损伤劣化过程,采用环境扫描电镜(ESEM)观察了耦合作用下的混凝土微观结构演变过程.结果表明,与单一硫酸盐侵蚀相比,弯曲荷载和干湿循环都加剧了混凝土在硫酸盐溶液中的损伤程度,但干湿循环的加速损伤作用更加明显.三因素耦合作用时,当荷载率低于40%时,干湿循环是加速混凝土损伤劣化的主要因素; 而当荷载率达到60%时,荷载引起的力学损伤是导致混凝土劣化的主要因素.试验还表明,在荷载-干湿交替耦合作用下,混凝土强度等级越高其抗硫酸盐侵蚀能力越强,硫酸盐浓度越大混凝土损伤越明显,粉煤灰和矿粉等矿物掺合料可显著提高混凝土抗硫酸盐侵蚀能力.
Abstract:
The damage process of concrete exposed to sulfate attack under flexural loading and drying-wetting cycles was systematically investigated. Environmental scanning electron microscopy(ESEM)was used to investigate the microstructure of interior concrete. The results indicate that compared with the single damage process of sulfate attack, flexural loading and wetting-drying cycles both accelerate the damage process of concrete under external sulfate attack, and the effect of the latter one is even more obvious. While coupled with the above three factors, the wetting-drying cycles and loading play the major role in the process of concrete degradation when the flexural load ratio is less than 40% and up to 60%, respectively. In addition, under the coupling effect of loading and wetting-drying cycles, strength grade and sulfate concentration can significantly affect the damage degree of concrete, and mineral admixtures can obviously improve the ability of sulfate resistance of concrete.

参考文献/References:

[1] Roziere E,Loukili A,El Hachem R,et al.Durability of concrete exposed to leaching and external sulphate attacks [J].Cement and Concrete Research,2009,39(12):1188-1198.
[2] Sarkar S,Mahadevan S,Meeussen J C L,et al.Numerical simulation of cementitious materials degradation under external sulfate attack [J].Cement and Concrete Composites,2010,32(3):241-252.
[3] Çavdar Ahmet,Yetgin 瘙塁ükrü.Investigation of mechanical and mineralogical properties of mortars subjected to sulfate [J].Construction and Building Materials,2010,24(1):2231-2242.
[4] Najimi M,Sobhani J,Pourkhorshidi A R.Durability of copper slag contained concrete exposed to sulfate attack [J].Construction and Building Materials,2011,25(4):1895-1905.
[5] Werner Klaus-Christian,Chen Yaoxing,Odler Ivan.Investigations on stress corrosion of hardened cement pastes[J].Cement and Concrete Research,2000,30(9):1443-1451.
[6] 黄战,邢锋,董必钦,等.荷载作用下的混凝土硫酸盐腐蚀研究[J].混凝土,2008(2):66-69.
  Huang Zhan,Xing Feng,Dong Biqin,et al.Study on the sulfate corrosion of concrete under the action of loading [J].Concrete,2008(2):66-69.(in Chinese)
[7] Jin Zuquan,Sun Wei,Jiang Jinyang,et al.Damage of concrete attacked by sulfate and sustained loading[J].Journal of Southeast University:English Edition,2008,24(1):69-73.
[8] 袁晓露,李北星,崔巩,等.干湿循环-硫酸盐侵蚀下混凝土损伤机理的分析[J].公路,2009(2):163-166.
  Yuan Xiaolu,Li Beixing,Cui Gong,et al.Analysis of damage mechanism for concrete exposed to wetting-drying and sulfate environment[J].Highway,2009(2):163-166.(in Chinese)
[9] Bassuoni M T,Nehdi M L.Durability of self-consolidating concrete to different exposure regimes of sodium sulfate attack [J].Materials and Structures,2009,42(8):1039-1057.
[10] Aye Thidar,Oguchi Chiaki T.Resistance of plain and blended cement mortars exposed to severe sulfate attacks [J].Construction and Building Materials,2011,25(6):2988-2996.

相似文献/References:

[1]常洪雷,金祖权.无碳化影响时干湿交替下水泥基材料中氯离子传输行为[J].东南大学学报(自然科学版),2019,49(6):1153.[doi:10.3969/j.issn.1001-0505.2019.06.019]
 Chang Honglei,Jin Zuquan.Chloride transport behavior in cementitious-based materials under cyclic drying-wetting condition without influence of carbonation[J].Journal of Southeast University (Natural Science Edition),2019,49(3):1153.[doi:10.3969/j.issn.1001-0505.2019.06.019]

备注/Memo

备注/Memo:
作者简介: 余振新(1987—),男,硕士生; 高建明(联系人),男,博士,教授,博士生导师,jmgao@seu.edu.cn.
基金项目: 国家重点基础研究发展计划(973计划)资助项目(2009CB623203).
引文格式: 余振新,高建明,宋鲁光,等.荷载-干湿交替-硫酸盐耦合作用下混凝土损伤过程[J].东南大学学报:自然科学版,2012,42(3):487-491. [doi:10.3969/j.issn.1001-0505.2012.03.018]
更新日期/Last Update: 2012-05-20