[1]王康,吴佰建,李兆霞.损伤跨尺度演化导致的混凝土强度尺寸效应[J].东南大学学报(自然科学版),2014,44(6):1230-1234.[doi:10.3969/j.issn.1001-0505.2014.06.024]
 Wang Kang,Wu Baijian,Li Zhaoxia.Size effect on concrete strength caused by trans-scale damage evolution[J].Journal of Southeast University (Natural Science Edition),2014,44(6):1230-1234.[doi:10.3969/j.issn.1001-0505.2014.06.024]
点击复制

损伤跨尺度演化导致的混凝土强度尺寸效应()
分享到:

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
44
期数:
2014年第6期
页码:
1230-1234
栏目:
数学、物理学、力学
出版日期:
2014-11-20

文章信息/Info

Title:
Size effect on concrete strength caused by trans-scale damage evolution
作者:
王康吴佰建李兆霞
东南大学土木工程学院, 南京210096
Author(s):
Wang Kang Wu Baijian Li Zhaoxia
School of Civil Engineering, Southeast University, Nanjing 210096, China
关键词:
混凝土 损伤跨尺度演化 微裂纹模型 多尺度建模 尺寸效应
Keywords:
concrete trans-scale damage evolution micro-crack model multi-scale modeling size effect
分类号:
O346.1
DOI:
10.3969/j.issn.1001-0505.2014.06.024
摘要:
基于直接从混凝土破坏机理出发建立的混凝土材料微裂纹模型,对不同尺寸的混凝土三点弯梁试样进行了多尺度建模,对损伤演化导致的试样破坏进行了数值仿真分析,探讨了混凝土尺寸效应的发生机理.研究结果表明:混凝土材料微裂纹模型能成功模拟混凝土中微裂纹分布式生长、聚合、宏观裂纹形成与扩展、试样破坏的全过程;随着混凝土梁试样尺寸的增大,试样中的微裂纹数目及其分布的随机性也随之增加;这些裂纹在微细观尺度上的无序效应在损伤跨尺度演化过程中被放大,导致混凝土试样的宏观力学行为随之变化,即强度减小,断裂能增大,宏观性能的离散度减小;损伤跨尺度的非线性串级发展是导致混凝土强度尺寸效应的根源;相较于Bazant尺寸效应,模拟结果更符合Carpinteri多重分形尺寸效应律.
Abstract:
Based on the micro-crack model established directly from the failure mechanism of concrete material, the concrete three-point bending beam specimens with different length scales were multi-scale modeled. The damage evolution leading to samples’ failure was numerically simulated and the mechanism of the size effect of concrete was discussed. The results show that the micro-crack model can successfully simulate the whole process of rupture, including the growth and aggregation of distributed micro-cracks, formation and propagation of macro-crack, and broken of the sample. The number of micro-cracks as well as their distribution randomness in the sample increase with the increase of the size of the concrete beam. The disorder effect of these cracks in the micro-scale view is amplified during the cross-scale damage evolution, inducing the change of macro-mechanical behaviors of the concrete specimen, i.e. the increase of the fracture energy and the decrease of the strength and the discreteness of macroscopic properties. The concrete size effect results from the trans-scale nonlinear damage progress. Compared with the Bazant size effect theory, the simulation results are more consistent with the Carpinteri’s size effect theory.

参考文献/References:

[1] Hillerborg A, Modéer M, Petersson P E. Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements[J]. Cement and Concrete Research, 1976, 6(6): 773-781.
[2] Shahbeyk S, Hosseini M, Yaghoobi M. Mesoscale finite element prediction of concrete failure [J]. Computational Materials Science, 2011, 50(7): 1973-1990.
[3] 吴佰建, 李兆霞, 汤可可. 大型土木结构多尺度模拟与损伤分析——从材料多尺度力学到结构多尺度力学[J]. 力学进展, 2007, 37(3): 321-336.
  Wu Baijian, Li Zhaoxia, Tang Keke. Multi-scale modeling and damage analysis of large civil structure—multi-scale mechanics from material to structure [J]. Advances in Mechanics, 2007, 37(3): 321-336.(in Chinese)
[4] Bazant Z P, Xu K. Size effect in fatigue fracture of concrete [J]. ACI Materials Journal, 1991, 88(4): 390-399.
[5] Grassl P, Grégoire D, Rojas Solano L, et al. Meso-scale modeling of the size effect on the fracture process zone of concrete [J]. International Journal of Solids and Structures, 2012, 49(13): 1818-1827.
[6] Ba?ant Z P, Yu Q, Hoover C G, et al. Non-uniqueness in softening damage and cohesive fracture models for concrete or bone caused by ignoring the size effect[C]//Proceedings of the 20th Analysis and Computation Specialty Conference. Chicago, IL, USA,2012: 418-424.
[7] Schlangen E, Garboczi E J. Fracture simulations of concrete using lattice models: Computational aspects [J]. Engineering Fracture Mechanics, 1997, 57(2): 319-332.
[8] Bazant Z P, Tabbara M R, Kazemi M T, et al. Random particle model for fracture of aggregate or fiber composites [J]. Journal of Engineering Mechanics, 1990, 116(8): 1686-1705.
[9] Bazant Z P, Oh B H. Microplane model for progressive fracture of concrete and rock [J]. Journal of Engineering Mechanics, 1985, 111(4): 559-582.
[10] 吴佰建, 李兆霞, 郭力. 模拟混凝土破坏过程的微裂纹模型及其应用[J]. 东南大学学报:自然科学版, 2013, 43(5):1034-1038.
  Wu Baijian, Li Zhaoxia, Guo Li. Micro-crack model for concrete rupture modeling and its applications[J]. Journal of Southeast University:Nature Science Edition, 2013, 43(5): 1034-1038.(in Chinese)
[11] Krajcinovic D, Fanella D. A micromechanical damage model for concrete [J]. Engineering Fracture Mechanics, 1986, 25(5): 585-596.
[12] Rilem D. Determination of the fracture energy of mortar and concrete by means of three-point bend tests on notched beames[J]. Materials and Structures, 1985, 18(106): 285-290.
[13] 何国威,夏蒙棼,柯孚久,等.多尺度耦合现象:挑战和机遇[J].自然科学进展,2004,14(2):121-123.

相似文献/References:

[1]李富民,袁迎曙,杜健民,等.氯盐腐蚀钢绞线的受拉性能退化特征[J].东南大学学报(自然科学版),2009,39(2):340.[doi:10.3969/j.issn.1001-0505.2009.02.028]
 Li Fumin,Yuan Yingshu,Du Jianmin,et al.Deterioration of tensile behavior of steel strands corroded by chloride[J].Journal of Southeast University (Natural Science Edition),2009,39(6):340.[doi:10.3969/j.issn.1001-0505.2009.02.028]
[2]金祖权,孙伟,侯保荣,等.混凝土的高温变形与微结构演化[J].东南大学学报(自然科学版),2010,40(3):619.[doi:10.3969/j.issn.1001-0505.2010.03.035]
 Jin Zuquan,Sun Wei,Hou Baorong,et al.Deformation and microstructure evolution of concrete subjected to elevated temperature[J].Journal of Southeast University (Natural Science Edition),2010,40(6):619.[doi:10.3969/j.issn.1001-0505.2010.03.035]
[3]潘华,邱洪兴.基于损伤力学的混凝土疲劳损伤模型[J].东南大学学报(自然科学版),2006,36(4):605.[doi:10.3969/j.issn.1001-0505.2006.04.023]
 Pan Hua,Qiu Hongxing.Fatigue model of concrete based on continuum damage mechanics[J].Journal of Southeast University (Natural Science Edition),2006,36(6):605.[doi:10.3969/j.issn.1001-0505.2006.04.023]
[4]耿飞,钱春香.图像分析技术在混凝土塑性收缩裂缝定量测试与评价中的应用研究[J].东南大学学报(自然科学版),2003,33(6):773.[doi:10.3969/j.issn.1001-0505.2003.06.022]
 Geng Fei,Qian Chunxiang.Image analysis technique for quantitative testing and evaluation of plastic shrinkage cracks in concrete[J].Journal of Southeast University (Natural Science Edition),2003,33(6):773.[doi:10.3969/j.issn.1001-0505.2003.06.022]
[5]余红发,孙伟,麻海燕,等.盐湖地区钢筋混凝土结构使用寿命的预测模型及其应用[J].东南大学学报(自然科学版),2002,32(4):638.[doi:10.3969/j.issn.1001-0505.2002.04.023]
 Yu Hongfa,Sun Wei,Ma Haiyan,et al.Prediction model for service life of reinforced concrete structures in salt lakes and its applications[J].Journal of Southeast University (Natural Science Edition),2002,32(6):638.[doi:10.3969/j.issn.1001-0505.2002.04.023]
[6]田正宏,白凯国,朱静.透水模板布改善混凝土表层质量试验研究[J].东南大学学报(自然科学版),2008,38(1):146.[doi:10.3969/j.issn.1001-0505.2008.01.028]
 Tian Zhenhong,Bai Kaiguo,Zhu Jing.Study on surface quality of concrete improved by infiltrating formwork texture[J].Journal of Southeast University (Natural Science Edition),2008,38(6):146.[doi:10.3969/j.issn.1001-0505.2008.01.028]
[7]汪基伟,陈玉泉.平面应变混凝土强度变形试验与等效单轴应变本构模型[J].东南大学学报(自然科学版),2005,35(5):775.[doi:10.3969/j.issn.1001-0505.2005.05.026]
 Wang Jiwei,Chen Yuquan.Strength-deformation test and equivalent uniaxial constitutive model of concrete in plane strain[J].Journal of Southeast University (Natural Science Edition),2005,35(6):775.[doi:10.3969/j.issn.1001-0505.2005.05.026]
[8]余红发,孙伟,王甲春,等.盐湖地区侵蚀性离子在混凝土中的扩散及其相互作用[J].东南大学学报(自然科学版),2003,33(2):156.[doi:10.3969/j.issn.1001-0505.2003.02.010]
 Yu Hongfa,Sun Wei,Wang Jiachun,et al.Diffusion of corrosive ions into concrete exposed to salt lake and interaction between corrosive-ions and concrete[J].Journal of Southeast University (Natural Science Edition),2003,33(6):156.[doi:10.3969/j.issn.1001-0505.2003.02.010]
[9]高建明,孙伟.钢纤维砼抗折疲劳寿命分布规律的研究[J].东南大学学报(自然科学版),1997,27(1):96.[doi:10.3969/j.issn.1001-0505.1997.01.020]
 [J].Journal of Southeast University (Natural Science Edition),1997,27(6):96.[doi:10.3969/j.issn.1001-0505.1997.01.020]
[10]樊华,宋启根.用统计连续理论研究混凝土的力学性能[J].东南大学学报(自然科学版),1996,26(6):64.[doi:10.3969/j.issn.1001-0505.1996.06.013]
 Fan Hua,Song Qigen.Study of Mechanical Properties of Concrete on the Statictical Continuum Theory[J].Journal of Southeast University (Natural Science Edition),1996,26(6):64.[doi:10.3969/j.issn.1001-0505.1996.06.013]

备注/Memo

备注/Memo:
收稿日期: 2014-06-22.
作者简介: 王康(1989—),男,硕士生;李兆霞(联系人),女,博士,教授,博士生导师,zhxli@seu.edu.cn.
基金项目: 国家自然科学基金资助项目(11072060).
引用本文: 王康,吴佰建,李兆霞.损伤跨尺度演化导致的混凝土强度尺寸效应[J].东南大学学报:自然科学版,2014,44(6):1230-1234. [doi:10.3969/j.issn.1001-0505.2014.06.024]
更新日期/Last Update: 2014-11-20