[1]钱春香,黄蓓,董华.集料尺寸和形状及掺合料对混凝土界面的影响[J].东南大学学报(自然科学版),2009,39(4):840-843.[doi:10.3969/j.issn.1001-0505.2009.04.037]
　Qian Chunxiang,Huang Bei,Dong Hua.Influence of size and shape of aggregate and mineral admixture on interface of concrete[J].Journal of Southeast University (Natural Science Edition),2009,39(4):840-843.[doi:10.3969/j.issn.1001-0505.2009.04.037]
点击复制

集料尺寸和形状及掺合料对混凝土界面的影响()
分享到：

《东南大学学报(自然科学版)》[ISSN:1001-0505/CN:32-1178/N]

卷:
39
期数:
2009年第4期
页码:
840-843
栏目:
材料科学与工程
出版日期:
2009-07-20

文章信息/Info

Title:
Influence of size and shape of aggregate and mineral admixture on interface of concrete
作者:
钱春香;  黄蓓;  董华
东南大学材料科学与工程学院,南京 211189; 东南大学江苏省土木工程材料重点实验室,南京 211189
Author(s):
Qian Chunxiang;  Huang Bei;  Dong Hua
School of Materials Science and Engineering, Southeast University, Nanjing 211189,China
Jiangsu Key Laboratory of Construction Materials, Southeast University, Nanjing 211189, China
关键词:
集料形状;  集料尺寸;  界面;  石灰石粉;  粉煤灰
Keywords:
aggregate shape;  aggregate size;  interface;  limestone powder;  fly ash
分类号:
TU528
DOI:
10.3969/j.issn.1001-0505.2009.04.037
摘要:
研究混凝土粗集料与砂浆在宏观尺度上的界面特性,并采用砂浆中的砂粒与粗集料的平均间距(简称界面平均间距)进行表征.结合雅砻江锦屏大坝集料品种,研究了球形和片状2种粗集料形状、2组粗集料尺寸,以及粉煤灰和石灰石粉的2个掺量(10%,20%)对界面平均间距的影响.结果表明,采用界面区砂粒与粗集料的平均间距能较好地反映界面区的宏观离析和均质性,测量使用也较简便.对于球形集料,大、小集料上方与下方的界面平均间距无显著差异,表明界面较均匀,离析不明显; 而对于片状集料,随着尺寸增大,上、下方的界面平均间距的差异增大,表明大的片状集料下方产生了明显的离析.研究结果还表明,采用粉煤灰或石灰石粉部分等质量取代水泥,可以改善片状集料下方浆体的离析.
Abstract:
The interfacial characteristics between coarse aggregates and mortar matrix are studied and characterized by the average distance between sand and coarse aggregates(briefly, average interfacial distance). The effects of the coarse aggregates with different shapes(sphere and patch)and sizes, as well as the fly ash and limestone powder on the interfacial average distance are investigated. Results show that the method of measuring the average interfacial distance can not only better reflect the homogeneity of interfacial transition zone(ITZ)but also be used simply and conveniently. The sphere aggregates with different sizes have similar average interfacial distances, which demonstrates that the interfaces are uniform. While for the patch ones, the differences of the average interfacial distances above and below the coarse aggregate become obvious with the increase of the size of aggregates, which demonstrates that significant bleeding appears at the downside of coarse aggregates. The research also shows that the addition of limestone powder or fly ash can improve the bleeding.

参考文献/References:

[1] Chen H S,Sun W,Stroeven P,et al.Overestimation of the interface thickness around convex-shaped grain by sectional analysis[J]. Acta Materialia,2007,55(11):3943-3949.
[2] Diamond S.Considerations in image analysis as applied to investigations of the ITZ in concrete[J].Cement and Concrete Composites,2001,23(2/3):171-178.
[3] Elsharief A,Cohen M D,Olek J.Influence of aggregate size,water cement ratio and age on the microstructure of the interfacial transition zone[J]. Cement and Concrete Research,2003,33(11):1837-1849.
[4] Belaid F,Arliguie G,Francois R.Porous structure of the ITZ around galvanized and ordinary steel reinforcements[J].Cement and Concrete Research,2001,31(11):1561-1566.
[5] Scrivener Karen L.Backscattered electron imaging of cementitious microstructures:understanding and quantification[J]. Cement and Concrete Composites,2004,26(8):935-945.
[6] Zhang M H,Lastra R,Malhotra V M.Rice-husk ash paste and concrete:some aspects of hydration and the microstructure of the interfacial zone between the aggregate and paste[J]. Cement and Concrete Research,1996,26(6):963-977.
[7] Ollivier J P,Maso J C,Bourdette B.Interfacial transition zone in concrete[J].Advanced Cement Based Materials,1995,2(1):30-38.
[8] Igarashi S,Bentur A,Mindess S.Microhardness testing of cementitious materials[J].Advanced Cement Based Materials,1996,4(2):48-57.
[9] 连丽,印海春,廖卫东.混凝土界面区的显微硬度研究[J].国外建材科技,2005,26(2):8-11.
　 Lian Li,Yin Haichun,Liao Weidong.Microhardness testing of interfacial transition zone in concrete [J].Science and Technology of Overseas Buildings,2005,26(2):8-11.(in Chinese)
[10] Akcaoglu T,Tokyay M,Celik T.Effect of coarse aggregate size and matrix quality on ITZ and failure behavior of concrete under uniaxial compression[J].Cement and Concrete Composites,2004,26(6):633-638.
[11] Tasong W A,Lynsdale C J,Cripps J C.Aggregate-cement paste interface,part Ⅰ:influence of aggregate geochemistry[J]. Cement and Concrete Research,1999,29(7):1019-1025.
[12] Prokopski G,Halbiniak J.Interfacial transition zone in cementitious materials[J].Cement and Concrete Research,2000,30(4):579-583.
[13] Akcaoglu T,Tokyay M,Celik T.Effect of coarse aggregate size on interfacial cracking under uniaxial compression[J].Materials Letters,2002,57(4):828-833.
[14] Caliskan S.Aggregate/mortar interface:influence of silica fume at the micro-and macro-level[J]. Cement and Concrete Composites,2003,25(4/5):557-564.

备注/Memo

备注/Memo:
作者简介: 钱春香(1966—),女,博士,教授,博士生导师,cxqian@seu.edu.cn.
基金项目: 国家自然科学基金重点资助项目(50539040).
引文格式: 钱春香,黄蓓,董华.集料尺寸和形状及掺合料对混凝土界面的影响[J].东南大学学报:自然科学版,2009,39(4):840-843. [doi:10.3969/j.issn.1001-0505.2009.04.037]
更新日期/Last Update: 2009-07-20